VERBATIM 3D Printer Filament PET-G 2,85mm ,123m, 1000g white

Kód: 32976

Part No.: 55058

Dostupnosť: zvyčajne do 24hodin

Výrobca: Verbatim

Bežná cena: 22,80 € s DPH

Vaša cena: 22,10 € s DPH / 18,42 € bez DPH

Nákupom získate 221 bonusových bodov.

Počet:

Features

Strong, high clarity, odour neutral and easy-to-print filament
High impact strength
Excellent flexibility
Almost no warping or shrinkage
Hydrophobic (does not absorb water)
Food packaging grade pellets used
Main applications: Concept modelling for mechanics, medical, food containers, transparent objects.

TECHNICAL SPECIFICATIONS

Diameter	2.85 mm ± 0.10 mm
Roundness	>95%
RAL	9003
Weight	1000 g
Color	white

MATERIAL PROPERTIES
Specific gravity	1.27g/cc (Test method: ISO 1183)
MFR 190°C/2.16 kg	6.4 gr/10 min (Test method: ISO 1133)
Tensile strength at yield	50 mPa
Strain at yield	5% (Test method: ISO 527)
Strain at break	23% (Test method: ISO 527)
Tensile modulus	2020 MPa (Test method: ISO 527)
Flexural modulus	2050 MPa (Test method: ISO 178)
Flexural strength	69 MPa (Test method: ISO 178)
Impact strength - Charpy method 23°C	8.1 kJ/m2 (Test method: ISO 179)
Rockwell Hardness	105 (Test method: ASTM D785)
Moisture absorption	1104 ppm (Test method: ISO 62)
Printing temperature	240±10°C
Heat deflection temperature	70°C (Test metod: ASTM 648)
Transparency	90% (Test method: ASTM D1003)

Popis produktu

Features

Strong, high clarity, odour neutral and easy-to-print filament
High impact strength
Excellent flexibility
Almost no warping or shrinkage
Hydrophobic (does not absorb water)
Food packaging grade pellets used
Main applications: Concept modelling for mechanics, medical, food containers, transparent objects.

TECHNICAL SPECIFICATIONS

Diameter	2.85 mm ± 0.10 mm
Roundness	>95%
RAL	9003
Weight	1000 g
Color	white

MATERIAL PROPERTIES
Specific gravity	1.27g/cc (Test method: ISO 1183)
MFR 190°C/2.16 kg	6.4 gr/10 min (Test method: ISO 1133)
Tensile strength at yield	50 mPa
Strain at yield	5% (Test method: ISO 527)
Strain at break	23% (Test method: ISO 527)
Tensile modulus	2020 MPa (Test method: ISO 527)
Flexural modulus	2050 MPa (Test method: ISO 178)
Flexural strength	69 MPa (Test method: ISO 178)
Impact strength - Charpy method 23°C	8.1 kJ/m2 (Test method: ISO 179)
Rockwell Hardness	105 (Test method: ASTM D785)
Moisture absorption	1104 ppm (Test method: ISO 62)
Printing temperature	240±10°C
Heat deflection temperature	70°C (Test metod: ASTM 648)
Transparency	90% (Test method: ASTM D1003)